Significantly Accelerated Spherulitic Growth Rates for
Semicrystalline Polymers through the Layer-by-Layer Film Method
Yaqiong Zhang,? Hongjun Xu,? Jingjing Yang,? Shouyu Chen,? Yunsheng Ding,? and Zhigang Wang*,?
?CAS Key Laboratory of Soft Matter Chemistry, Department of Polymer Science and Engineering, Hefei National Laboratory for
Physical Sciences at the Microscale, University of Science and Technology of China, Hefei, Anhui Province 230026, P. R. China
?Institute of Polymer Materials & Chemical Engineering, School of Chemical Engineering, Hefei University of Technology, Hefei,
Anhui Province 230009, P. R. China
摘要：很少有人思考過一層液態(tài)聚合物鋪敷在結(jié)晶聚合物表面會起到什么樣的效果。在這篇文章所報(bào)道的研究中我們主要是以偏光顯微鏡（POM）觀察一層聚環(huán)氧乙烷（PEO）膜覆蓋在聚乳酸（PLA）膜表面上，PEO熔體層對PLA在不同溫度下等溫結(jié)晶動力學(xué)的影響。我們將該PEO/PLA雙層膜與PLA膜和PLA/PEO共混物膜中PLA結(jié)晶動力學(xué)行為進(jìn)行了對比研究。非常有意思的是PEO熔體層可以顯著加快PLA球晶的生長速率。另一個重要發(fā)現(xiàn)是雙層膜中PLA竟然可以在接近PLA的玻璃化轉(zhuǎn)變溫度（Tg）處發(fā)生結(jié)晶。我們用調(diào)試差示掃描量熱法（MDSC）和動態(tài)機(jī)械分析法(DMA)分別測量PEO/PLA雙層膜的Tg變化, 由于PEO層的影響，PLA的Tg僅有輕微下降。我們用掃描電子顯微鏡(SEM)觀察了雙層膜的斷面，發(fā)現(xiàn)在PLA和PEO層間有不規(guī)則的界面擴(kuò)散層，該擴(kuò)散層對加快PLA球晶生長速率起著很大的作用。我們的研究結(jié)果表明其實(shí)可以用這種多層膜方法來代替共混法進(jìn)行聚乳酸等結(jié)晶聚合物的加工，減低能耗, 該方法有極大的潛在應(yīng)用價(jià)值。