Enhanced interfacial interaction of epoxy nanocomposites with activated graphene nanosheets
作者：Deng, Hui Wu, Fan Chen, Lei Xu, Zhiwei Liu, Liangsen Yang, Caiyun Mai, Wei Cheng, Bowen
關鍵字：graphene composites
論文來源：期刊
具體來源：Journal of Applied Polymer Science
發表時間：2014年
下載 （download）
The interfacial properties of epoxy nanocomposites reinforced by thermally exfoliated graphene nanosheets (TEG) and activated thermally exfoliated graphene nanosheets (a-TEG) were compared. The specific surface area (SSA) of a-TEG with well-defined micro-mesopore size distribution was 1000 m2/g, which was much higher that of TEG (550 m2/g). The interfacial interaction between a-TEG and epoxy was stronger than that of TEG/epoxy owing to their higher SSA and pore size which was proved by dynamic mechanical analysis. As a result, the tensile strength of a-TEG/epoxy was increased compared with that of TEG/epoxy for all concentrations. In particular, the tensile and flexural strength of a-TEG/epoxy was increased up to 20 and 50% in comparison to that of TEG/epoxy at 0.05 wt % graphene, respectively.