Mukun He#, Lei Zhang#, Kunpeng Ruan, Junliang Zhang, Haitian Zhang, Peng Lv, Yongqiang Guo, Xuetao Shi, Hua Guo*, Jie Kong and Junwei Gu*. Functionalized Aluminum Nitride for Improving Hydrolysis Resistances of Highly Thermally Conductive Polysiloxane Composites. Nano-Micro Letters, 2025, 17: 134. 2023IF=31.6.（1區材料科學Top期刊）
https://doi.org/10.1007/s40820-025-01669-5
Abstract
A series of divinylphenyl-acryloyl chloride copolymers (PDVB-co-PACl) is synthesized via atom transfer radical polymerization employing tert-butyl acrylate and divinylbenzene as monomers. PDVB-co-PACl is utilized to graft on the surface of spherical aluminum nitride (AlN) to prepare functionalized AlN (AlN@PDVB-co-PACl). Polymethylhydrosiloxane (PMHS) is then used as the matrix to prepare thermally conductive AlN@PDVB-co-PACl/PMHS composites with AlN@PDVB-co-PACl as fillers through blending and curing. The grafting of PDVB-co-PACl synchronously enhances the hydrolysis resistance of AlN and its interfacial compatibility with PMHS matrix. When the molecular weight of PDVB-co-PACl is 5100 g/mol and the grafting density is 0.8 wt%, the compositescontaining 75 wt% of AlN@PDVB-co-PACl exhibit the optimal comprehensive performance. The thermal conductivity (λ) of the composite is 1.14 W/(m·K), which enhances by 20% and 420% compared to the λ of simply physically blended AlN/PMHS composite and pure PMHS, respectively. Meanwhile, AlN@PDVB-co-PACl/PMHS composites display remarkable hydrothermal aging resistance by retaining 99.1% of its λ after soaking in 90℃ deionized water for 80 hours, whereas the λ of the blended AlN/PMHS composites decreases sharply to 93.7%.
本研究以丙烯酸叔丁酯為單體和二乙烯基苯為支化單元，通過原子轉移自由基聚合合成具有支化結構的二乙烯基苯-丙烯酰氯無規共聚物（PDVB-co-PACl）。以聚甲基氫硅氧烷（PMHS）為基體、PDVB-co-PACl表面接枝改性的AlN（AlN@PDVB-co-PACl）為導熱填料，經共混復合-熱固化制備AlN@PDVB-co-PACl/PMHS導熱復合材料。無規共聚物的成功接枝同步提升了AlN的耐水解性能及其與PMHS基體間的界面相容性。當PDVB-co-PACl分子量為5100 g/mol、AlN@PDVB-co-PACl的質量分數為75 wt%且其表面PDVB-co-PACl接枝量為0.8 wt%時，AlN@PDVB-co-PACl/PMHS導熱復合材料具有最優的綜合性能，其λ為1.14 W/(m·K)，較簡單共混AlN/PMHS和純PMHS的λ分別提升了20%和420%，且在90℃去離子水中浸泡80小時后的λ保持率為99.1%，明顯優于AlN/PMHS導熱復合材料同樣處理后的λ保持率（93.7%）。
論文亮點
1. 設計合成了提升AlN耐水解性的具有支化結構的二乙烯基苯-丙烯酰氯無規共聚物（PDVB-co-PACl）。
2. 優化PDVB-co-PACl分子量為5100 g/mol時，其具有最佳的耐水解性、最低的界面熱阻。
3. 當AlN@PDVB-co-PACl的質量分數為75 wt%且其表面PDVB-co-PACl接枝量為0.8 wt%時，AlN@PDVB-co-PACl/PMHS復合材料的λ為1.14 W/(m·K)，在90℃去離子水中浸泡80小時后λ保持率為99.1%。