| Preparation and heat treatment of semi-aromatic polyamide fiber |
| 關鍵詞： |
semi-aromatic polyamide fiber melt spinning heat treatment |
| 類 別： |
纖維 >> 合成纖維 |
| 來 源： |
ICAFPM 2011 |
| 資料類型： |
pdf文件 |
| 資料大小： |
1477K |
| 簡 介： |
Semi-aromatic polyamide has advantages of both aromatic and aliphatic polyamide. The semi-aromatic polyamide fiber was prepared using melting spinning rather than solution spinning in this article. Differential Scanning Calorimeter (DSC) and Thermogravimetric Analysis (TGA) were used to measure the crystallization and the thermal stability of the semi-aromatic polyamide before spinning. After heat treatment of the as-spun fiber under different temperatures, the tensile strength, Young’s modulus as well as elongation at break of the fiber were studied by tensile tester. By comparing the difference between the fibers before and after heat treatment, it was found that the fiber with heat treatment showed much better properties than the one without heat treatment. |
| 上傳人： |
epce |
| 上傳時間： |
2011-10-12 13:55:18 |
| 下載次數： |
6 |
| 消耗積分： |
4 |
| 我要收藏： |
 |
| |
友情提示：下載后對該資源進行評論，即可獎勵2分。 |
|
本欄目部分資源來自互聯網，僅為促進數據共享和信息交流，如有版權問題請告知本網或上傳者本人，本網會及時給予答復。 |
| 報告錯誤
1.下載無效
2. 資料明顯無價值
3. 資料重復存在
|